Qattiqlik nuqtai nazaridan, nikel odatda, aniq qadriyatlar poklik, qayta ishlash (.} {.} .} {.} {.} .} harorati, va harorati haqida batafsil taqqoslash:
Qattiqlik odatda brinell (HV), Viksk (HV) yoki RockWell (soat) . xona haroratida tozalang (Issiqlikni tozalash) metallari:
Pure copper has a Brinell hardness of approximately 35–45 HB, a Vickers hardness of 40–50 HV, and a Rockwell B hardness (HRB) of around 20–30. It is relatively soft and highly ductile, which makes it easy to form (e.g., into wires or sheets) but prone to deformation under moderate stress .
Toza nikel, taxminan 60-80 HV, 70-90 HV va deformatsiya 40 - {{6} {{}} bilan solishtirganda uni sezilarli darajada va deformatsiyaga chidamli bo'ladi
Ikkala metalni sovuq ishlash orqali qotib qolish mumkin (e {{. . . .} .} . .} {.} .} .} {.} rasmlarini kuchaytiradi, bu ularning kristall tuzilishida dislokatsiyalarni joriy etish orqali ularning qattiqligini oshiradi:
Sovuq ishlangan mis 100-140 Hb (deformatsiya darajasiga qarab), lekin shunga qaramay, u sovuq ishlangan nikelning qattiqligi oshadi .
Sovuq ishlangan nikel 150-200 HBning qattiqligi va .}}}}}}}}}
Nikelning yuqori qiymati, bu kasallikka chidamliligi yoki strukturaviy barqarorlikni talab qiladigan talablarga nisbatan ko'proq moslashtiradi, masalan:
Mashinalardagi tarkibiy qismlar (e {{{{.} .} tishlilar).
Mis yoki po'lat . singari softer metallarining qattiqligini oshirish uchun himoya qoplamalari (nikel plitka)
Mis, yumshoqroq bo'lganda, egiluvchanlik, o'tkazuvchanlik (elektr yoki issiqlik) yoki multipdatitsion juda muhim - masalan, elektr simlarida, issiqlik almashtirgichlari yoki dekorativ metalli .
Xulosa qilib aytganda, toza nikel toza misdan ko'ra qattiqroq va bu farq qayta ishlangan yoki yuk ko'taruvchi muhandislik dasturlari uchun nikel yaxshiroq mos keladi . .